SILIRUB S TRANSPARENT SILICONE 310 ml
76.9
/Cartridgeمتوفر
TECHNICAL SPECIFICATIONS:
Base: Polysiloxane
Consistency: Stable Paste
Drying System: Moisture cure
Texture formation(*) (20°C/65% relative humidity): Approx. 15 min.
Drying rate(*) (20°C/65% RH): Approx. 2mm/24 h
Hardness (DIN 53505): 20 ± 5 (according to Shore A test)
Specific gravity (DIN 53479): Approx. 1.02 g/ml
Maximum permissible decomposition: 25%
Temperature resistance (completely dry): -60°C to +180°C
Elastic recovery (ISO 7389): >90%
Modulus of elasticity 100% (DIN 53504): 0.40 N/mm2
Maximum tension (DIN 53504): 2.00 N/mm2
Elongation at break (DIN 53504): >500%
FEATURES:
– Very easy to apply
– Colorfast and UV resistant
– Permanent elasticity after hardening.
– Typical acetic odor
APPLICATIONS:
– In plumbing and kitchen joints
– Provides the best sealing in glass works
– In structural joints in humid environments
– Sealing in air conditioning systems
PACKAGING:
Color: Transparent
Packaging: Cartridge 310 mL
Shelf Life: At least 12 months in unopened packaging in a cool and dry storage area at temperatures between +5 ° C and +25 ° C.
JOINT SIZE:
Minimum Width: 5mm
Maximum Width: 30mm
Minimum Depth: 5mm
Recommendation: Joint width = 2 x joint depth
SURFACES:
Type: Can be used on all known building surfaces, ceramics, porcelain, glass surfaces. Not used on PVC and acrylic plates.
Surface condition: Clean, dry, dust and oil free
Pre-treatment: : In water filled applications, porous surfaces should be primed with Primer 150. Primer is not required on non-porous (smooth) surfaces.
We recommend a preliminary compatibility test
APPLICATION:
Method: Silicone Gun
Application temperature: +5°C to +35°C
Cleaning: Clean with white spirit immediately after use.
Finishing: Before tissue formation, with soapy solution
Repair: With Silirub S
WARNINGS:
Due to its acetic character, some metals (copper, lead) may be affected.
Do not use this filler on natural stones such as marble etc. Use Silirub MA instead.
Contact between this material and the basic filler materials of double-glazed insulating windows or PVB films of safety glass should be avoided.
Base: Polysiloxane
Consistency: Stable Paste
Drying System: Moisture cure
Texture formation(*) (20°C/65% relative humidity): Approx. 15 min.
Drying rate(*) (20°C/65% RH): Approx. 2mm/24 h
Hardness (DIN 53505): 20 ± 5 (according to Shore A test)
Specific gravity (DIN 53479): Approx. 1.02 g/ml
Maximum permissible decomposition: 25%
Temperature resistance (completely dry): -60°C to +180°C
Elastic recovery (ISO 7389): >90%
Modulus of elasticity 100% (DIN 53504): 0.40 N/mm2
Maximum tension (DIN 53504): 2.00 N/mm2
Elongation at break (DIN 53504): >500%
FEATURES:
– Very easy to apply
– Colorfast and UV resistant
– Permanent elasticity after hardening.
– Typical acetic odor
APPLICATIONS:
– In plumbing and kitchen joints
– Provides the best sealing in glass works
– In structural joints in humid environments
– Sealing in air conditioning systems
PACKAGING:
Color: Transparent
Packaging: Cartridge 310 mL
Shelf Life: At least 12 months in unopened packaging in a cool and dry storage area at temperatures between +5 ° C and +25 ° C.
JOINT SIZE:
Minimum Width: 5mm
Maximum Width: 30mm
Minimum Depth: 5mm
Recommendation: Joint width = 2 x joint depth
SURFACES:
Type: Can be used on all known building surfaces, ceramics, porcelain, glass surfaces. Not used on PVC and acrylic plates.
Surface condition: Clean, dry, dust and oil free
Pre-treatment: : In water filled applications, porous surfaces should be primed with Primer 150. Primer is not required on non-porous (smooth) surfaces.
We recommend a preliminary compatibility test
APPLICATION:
Method: Silicone Gun
Application temperature: +5°C to +35°C
Cleaning: Clean with white spirit immediately after use.
Finishing: Before tissue formation, with soapy solution
Repair: With Silirub S
WARNINGS:
Due to its acetic character, some metals (copper, lead) may be affected.
Do not use this filler on natural stones such as marble etc. Use Silirub MA instead.
Contact between this material and the basic filler materials of double-glazed insulating windows or PVB films of safety glass should be avoided.